Detail Description:

PROPERTIES:

• Excellent solubility in the principle refrigerant over a wide compressor temperature range of operation, resulting in an absence of lubricant pool formation and hence maintained compressor efficiency.
• Chemical and thermal stability. Exposure to high temperature and high levels of moisture results in minimised product degradation, which when compared to POE (polyol esters) can release corrosive acids and cause a loss of performance and possible failures
• Excellent Viscosity Index (>200), the higher viscosity index ensures that at higher temperature there is sufficient lubricant film thickness in hydrodynamic conditions to enhance compressor life and efficiency. This can also be used by compressor manufacturers to select a lower viscosity grades to get power savings.
• Superior lubricity compared to POE which is reflected in higher FALEX failure loads and low 4 ball wear scar dia.
• Material compatibility, common seal and gasket materials are unaffected by PAG. The elastomers commonly found in R 134a system are compatible with PAGs. However incompatibility with certain alkyd paints and resins results in internal systems either unpainted or coated with resistant materials like epoxy resin based paints.
• Miscibility with refrigerants, the miscibility of refrigerants is measured by critical solution temperature and within the methods (ASHRAE 86), SEETUL RFL grades remain fully miscible within the limits of -60°C to 100°C over the full range tested (1 - 30%).
• Chemical stability, when tested according to ASHRAE std. 97-1983 (sealed glass tube), the chemical stability of PAG based product was found better than POE product even in the presence of 1 % water.
• Hydrolytic stability, both PAG and POE are bound to absorb moisture but hydrolysis may occur in case of POE leading to formation of acidic species, potentially leading to metallic corrosion, device blockage and reduced compressor efficiency. Rapid acid number increase in POE may be catalysed by metal contamination such as some types of brazing flux and plated system components. Despite their hygroscopic nature, PAGs will not hydrolyse and will demonstrate high water tolerance.
• Electric properties, specific resistivity when measured as per IEC 247 typically recorded a value of 108 -m, with breakdown voltages (IEC 156) being recorded as 50 - 70 kV.
• Miscibility and stability in R 12, the older systems using the R 12 gasses were evaluated and cSt over temperature range -40 to 100°C show no abnormality in ranger concentration of 1 - 30 %. Systems using R 12 as refrigerant use mineral oil as lubricant and SEETUL RFL grades are found compatible with residual mineral oils and R 12 grades.

INTRODUCTION: